Higher fracture toughness of tetragonal zirconia ceramics through nanocrystalline structure

TRUNEC, M. CHLUP, Z.

Originální název

Typ

článek v časopise ve Web of Science, Jimp

Jazyk

angličtina

Originální abstrakt

Fracture toughness of nanocrystalline zirconia ceramic stabilized with 1.5 mol.% Y2O3 was measured and compared with fracture toughness of submicrometer-grained zirconia ceramics stabilized with 3 mol.% Y2O3. It was found that nanocrystalline ceramics demonstrated higher fracture toughness than submicrometer-grained zirconia ceramics with both optimized and common grain sizes. The high fracture toughness of nanocrystalline zirconia was confirmed by two different testing methods: indentation method (15.5 MPa m0.5) and chevron notched beam method (7.9 MPa m0.5).

Klíčová slova

Zirconia; Nanocrystalline materials; Coarsening; Toughness; Martensitic phase transformation

Autoři

TRUNEC, M.; CHLUP, Z.

Rok RIV

2009

Vydáno

1. 1. 2009

Nakladatel

PERGAMON-ELSEVIER SCIENCE LTD

Místo

THE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, ENGLAND

ISSN

1359-6462

Periodikum

SCRIPTA MATERIALIA

Ročník

Číslo

Stát

Spojené státy americké

Strany od

Strany do

Strany počet

BibTex

@article{BUT48843,
  author="Martin {Trunec} and Zdeněk {Chlup}",
  title="Higher fracture toughness of tetragonal zirconia ceramics through nanocrystalline structure",
  journal="SCRIPTA MATERIALIA",
  year="2009",
  volume="61",
  number="1",
  pages="56--59",
  issn="1359-6462"
}